Homogeneous Polymer Blend and Process of Making the Same

ABSTRACT

A homogeneous polymer blend comprises a thermoplastic first polymer having a crystallinity of at least 30%; and a second polymer having a crystallinity of more than 5% and being at least partially cross-linked.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Application No. 60/693,030, filed on Jun. 22, 2005. This application also claims priority to US regular patent applications (Attorney Docket Number 2005B157) filed Dec. 6, 2005 and (Attorney Docket Number 2005B160) filed Dec. 6, 2005.

FIELD

This invention relates to a homogeneous thermoplastic polymer blend, and to an in-reactor process of making such a polymer blend.

BACKGROUND

There is a significant ongoing effort to develop blends of different polymers so as to produce compositions having a desirable balance of properties and attributes, leading to enhanced products that are useful in a number of applications. Such enhancements include, but are not limited to, good tensile strength while still providing suitable mechanical recoverability (elastic recovery), impact strength, scratch resistance, and low compression set. As a result a wide variety of polymer blends are currently available, which depending on the miscibility of the components of the blend may be homogeneous (single phase) compositions or heterogeneous (multiple phase) compositions.

For example, U.S. Pat. No. 3,882,197 discloses homogeneous blends of stereoregular propylene/alpha-olefin copolymers, stereoregular propylene, and ethylene copolymer rubbers.

U.S. Pat. No. 3,888,949 discloses the synthesis of homogeneous blend compositions containing isotactic polypropylene and copolymers of propylene and an alpha-olefin, containing between 6-20 carbon atoms, which have improved elongation and tensile strength over either the copolymer or isotactic polypropylene. Copolymers of propylene and alpha-olefin are described wherein the alpha-olefin is hexene, octene or dodecene.

U.S. Pat. No. 6,635,715 discloses a composition formed by blending at least a first polymer component and a second polymer component, wherein the first polymer component comprises from about 2% to about 95% by weight of the blend and is formed from isotactic polypropylene having a melting point greater than about 110° C., wherein the second polymer component is produced by copolymerizing propylene and ethylene using a chiral metallocene catalyst system to produce a copolymer having a crystallinity from about 2% to about 65% from isotactic polypropylene sequences, a propylene content of from about 75% to about 90% by weight, a melting point of from 25 to 105° C., and wherein a glass transition temperature of said second polymer component is retained in the polymer blend.

None of the above disclosed blends use cross-linked semi-crystalline polymers, although thermoplastic blends with cross-linked polymers offer a number of advantages over uncross-linked blends, such as high impact strength, low compression set and scratch resistance. In fact, most thermoplastic blends with cross-linked polymers are currently heterogeneous (multiple phase) compositions.

Heterogeneous polymer blends generally comprise a matrix of a first polymer within which a second polymer is dispersed and, depending on the properties and the relative amounts of the first and second polymers, a wide variety of such polymer blends can be produced. Of particular interest are blends, also referred to as thermoplastic elastomers, in which the first polymer is a thermoplastic material, such as polypropylene, and the second polymer is an elastomeric material, such as an ethylene-propylene elastomer or an ethylene-propylene-diene (EPDM) rubber. The second polymer may or may not be cross-linked. Examples of such thermoplastic elastomers include polypropylene impact copolymers, thermoplastic olefins and thermoplastic vulcanizates. Unlike conventional vulcanized rubbers, thermoplastic elastomers can be processed and recycled like thermoplastic materials, yet have properties and performance similar to that of vulcanized rubber at service temperatures.

For example, U.S. Pat. No. 6,245,856 discloses a thermoplastic olefin composition comprising polypropylene, an ethylene-alpha olefin elastomer and a compatabilizer comprising an ethylene-propylene copolymer having a propylene content of greater than 80 weight percent. In the absence of the compatabilizer, the elastomer phase is said to be uneven with particles greater than 5 microns in size, whereas the addition of the compatabilizer is said to improve dispersion such that the elastomer phase has a particle size of about 1 micron. The elastomer phase of this heterogeneous polymer blend is not cross-linked.

One method of making polymer blends is by mixing two different polymers after they have been polymerized to achieve a target set of properties. However, this method is relatively expensive making it much more desirable to make blends by direct polymerization. Blending by direct polymerization typically uses multiple reactors in series, where the product from one reactor is fed to a second reactor having a different polymerizing environment, resulting in a final product that is an intimate mix of two different products.

For example, U.S. Pat. No. 6,207,756 describes a process for producing a blend of a continuous phase of a semi-crystalline plastic, such as polypropylene, and a discontinuous phase of an amorphous elastomer, such as a terpolymer of ethylene, a C₃-C₂₀ alpha olefin and a non-conjugated diene. The blends are produced in series reactors by producing a first polymer component in a first reactor, directing the effluent to a second reactor and producing the second polymer component in solution in the second reactor in the presence of the first polymeric component. U.S. Pat. No. 6,319,998 also discloses using series solution polymerizations to produce blends of ethylene copolymers. U.S. Pat. No. 6,770,714 discloses the use of parallel polymerizations to produce different polymeric components that are then blended through extrusion or using other conventional mixing equipment. One polymeric component is a propylene homopolymer or copolymer and the second polymeric component is an ethylene copolymer.

One particularly useful form of polymer blend is a thermoplastic vulcanizate (“TPV”), which comprises a thermoplastic resin matrix, such as polypropylene, within which are dispersed particles of a cured elastomeric material, such as an EPDM rubber. TPVs are normally produced by a process of “dynamic vulcanization”, which is a process of vulcanizing or cross-linking the elastomeric component during intimate, melt mixing of the blend with plasticizers (e.g. process oils), fillers, stabilizers, and a cross-linking system under high shear and above the melting point of the thermoplastic matrix. The mixing is typically done in a twin-screw extruder, to create a fine dispersion of the elastomeric material within the thermoplastic resin while the elastomeric material is cured. The levels of thermoplastic resin and plasticizer (oil) can be adjusted to produce grades having different profiles of hardness, rheology and engineering properties, although in general it is difficult to produce TPVs by dynamic vulcanization in which the content of the elastomeric phase is greater than 50 wt % of the overall polymer blend. Examples of dynamic vulcanization are described in the U.S. Pat. Nos. 4,130,535 and 4,311,628.

However, while dynamic vulcanization is effective in producing TPVs with a unique profile of properties, it is expensive and suffers from a number of disadvantages. Thus the production of quality product is technically challenging and specialized equipment is needed. Moreover, the process involves many steps, each one critical to the eventual quality of the final product. Forming the polymer blend normally involves separately comminuting bales of the elastomeric polymer (which is typically how EPDM rubber is commercially distributed), mechanically mixing it with the thermoplastic resin along with the processing oils, curatives, and other ingredients in a suitable high shear mixing device to comminute the rubber particles and cure them to generate cured rubber particles embedded in a continuous thermoplastic resin matrix. The cured rubber particles in the finished products have an averaged particle size of 1 to 10 microns. Careful injection of processing oil helps manage the rheological characteristics of the fluid in the reactive extruder (to minimize pressure buildup) as well as product properties such as hardness. Precise control over the size and distribution of the cross-linked elastomer particles is sought, as it affects properties such as elastic recovery (as measured through compression set). While the products produced with existing technology have many desirable properties, there are gaps in the overall properties profile. Some of these are the need for higher service temperatures, improved elastic recovery, softer products, higher tensile strength, easier processability, oil-free compositions, and/or colorless products.

An improved process for producing TPVs is disclosed in U.S. Pat. No. 6,388,016, incorporated herein in its entirety, in which a polymer blend is produced by solution polymerization in series reactors employing metallocene catalysts and the resultant blend is subjected to dynamic vulcanization. In particular, the process involves feeding a first set of monomers selected from ethylene and higher alpha-olefins, and a solvent, to a first continuous flow stirred tank reactor, adding a metallocene catalyst to the first reactor in an amount of 50 to 100 weight % of the total amount of catalyst added to all reactors, operating the first reactor to polymerize the monomers to produce an effluent containing a first polymer, feeding the effluent from the first reactor to a second continuous flow stirred tank reactor, feeding a second set of monomers selected from ethylene, higher alpha-olefins and non-conjugated dienes, and optionally additional solvent, to the second reactor, operating the second reactor to polymerize the second monomers to produce a second polymer containing diene, recovering the resulting first and second polymers and blending them with a curing agent under conditions of heat and shear sufficient to cause the blend to flow and to at least partially crosslink the diene-containing polymer and form a dispersion of cured diene-containing particles in a matrix of the first polymer. It will, however, be seen that this improved process still relies on dynamic vulcanization to cure the elastomeric component.

According to the present invention it has now been found that a homogeneous polymer blend comprising an at least partially cross-linked polymeric component can be produced by an in-reactor blending and cross-linking method.

SUMMARY

In one aspect, the present invention resides in a homogeneous polymer blend comprising:

(a) a thermoplastic first polymer having a crystallinity of at least 30%; and

(b) a second polymer having a crystallinity of more than 5% and being at least partially cross-linked.

Conveniently, the second polymer is less crystalline than the thermoplastic first polymer, with crystallinity difference between the first polymer and the second polymer typically being less than 20%.

Conveniently, the thermoplastic first polymer comprises propylene and from 0 to 5 weight % alpha-olefin comonomer (based upon the weight of the polymer).

Conveniently, the thermoplastic first polymer has a melting point between 100 and 170° C. and a melt flow rate of 2000 dg/min or less (preferably 100 dg/min or less).

Conveniently, the second polymer is produced from a plurality of comonomers comprising at least one C₂ to C₂₀ olefin and at least one polyene. Conveniently, the polyene has at least two polymerizable unsaturated groups and preferably is a diene.

Conveniently, the second polymer comprises propylene and from 2 to 15 weight % of one or more C₂ and/or C₄ to C₁₀ alpha-olefin comonomers.

Preferably, the second polymer is an ethylene propylene copolymer, such as an ethylene propylene thermoplastic elastomer.

Preferably, said polymer blend is substantially free of processing oil and/or a curative agent.

In a another aspect, the present invention resides in a process for producing a homogeneous polymer blend comprising (a) a thermoplastic first polymer having at least 30% crystallinity; and (b) a second polymer different from the first polymer and having a crystallinity less than that of the first polymer, the second polymer being at least partially cross-linked, the process comprising:

(i) polymerizing at least one first monomer to produce the thermoplastic first polymer; and

(ii) contacting at least part of said first polymer with at least one second monomer and at least one polyene under conditions sufficient to polymerize said second monomer to produce said second polymer and simultaneously cross-link said second polymer such that the product of said contacting (ii) comprises at least a fraction which is insoluble in xylene.

In still a further aspect, the present invention resides in a process for producing a homogeneous polymer blend, the process comprising:

(a) selecting a catalyst capable of polymerizing a C₂ to C₂₀ olefin to produce a first polymer having at least 30% crystallinity;

(b) contacting said catalyst with one or more C₂ to C₂₀ olefins at a temperature of at least 50° C. to produce a first polymer having at least 30% crystallinity;

(c) contacting said first polymer and said catalyst with a monomer mixture comprising at least 15 wt % of one or more C₃ to C₂₀ olefins and at least 0.0001 wt % of at least one polyene under conditions sufficient to polymerize said one or more C₃ to C₂₀ olefins to produce a second polymer and simultaneously cross-link said second polymer.

Conveniently, said polyene has at least two polymerizable unsaturated groups.

Conveniently, said catalyst selected in (a) is a single site catalyst comprising at least one catalyst component, normally a metallocene, and at least one activator.

In still yet a further aspect, the present invention resides in a process for producing a homogeneous polymer blend, the process comprising:

(a) selecting a catalyst capable of polymerizing a C₂ to C₂₀ olefin to produce a first polymer having at least 30% crystallinity;

(b) contacting said catalyst with one or more C₂ to C₂₀ olefins at a temperature of at least 50° C. to produce a first polymer having at least 30% crystallinity;

(c) contacting said first polymer with a monomer mixture comprising at least 15 wt % of one or more C₃ to C₂₀ olefins and at least 0.0001 wt % of at least one polyene in the presence of a catalyst capable of polymerizing bulky monomers under conditions sufficient to polymerize said one or more C₃ to C₂₀ olefins to produce a second polymer and simultaneously cross-link said second polymer.

In one embodiment, the catalyst employed in contacting (c) is the same as the catalyst employed in contacting (b).

In another embodiment, the catalyst employed in contacting (c) is the different from the catalyst employed in contacting (b) and catalyst quenching is applied between the contacting (b) and the contacting (c).

DESCRIPTION OF THE DRAWINGS

FIG. 1A is an atomic force micrographs (AFM) of the polymer blend produced in Example 1 (image size is 20 by 20 microns).

FIG. 1B shows the trace of tan δ vs. temperature obtained from DMTA for the in-reactor blend produced in Example 1.

FIG. 2A is an atomic force micrographs (AFM) of the polymer blend produced in Example 2 (image size is 20 by 20 microns).

DETAILED DESCRIPTION

For purposes of this invention and the claims thereto when a polymer or oligomer is referred to as comprising an olefin, the olefin present in the polymer or oligomer is the polymerized or oligomerized form of the olefin, respectively. Likewise the use of the term polymer is meant to encompass homopolymers and copolymers. In addition the term copolymer includes any polymer having 2 or more monomers. Thus, as used herein, the term “polypropylene” means a polymer made of at least 50 weight % propylene units, preferably at least 70% propylene units, more preferably at least 80% propylene units, even more preferably at least 90% propylene units, even more preferably at least 95% propylene units or 100% propylene units.

As used herein, the term “homogeneous blend” is a composition having substantially one morphological phase in the same state. For example a blend of two polymers where one polymer is miscible with another polymer is said to be homogeneous in the solid state. Such morphology is determined using AFM or scanning electron microscopy (SEM). By miscible is meant that the blend of two or more polymers exhibits single-phase behavior for the glass transition temperature, e.g. the Tg would exist as a single, sharp transition temperature on a dynamic mechanical thermal analyzer (DMTA) trace of tan δ (the ratio of loss modulus to the storage modulus) versus temperature. By contrast, two separate transition temperatures would be observed for an immiscible blend, typically corresponding to the temperatures for each of the individual components of the blend. Thus a polymer blend is miscible when there is one Tg indicated on the DMTA trace. A miscible blend is homogeneous, while an immiscible blend is heterogeneous.

In contract, the term “heterogeneous blend” means a composition having two or more morphological phases in the same state. For example a blend of two polymers where one polymer forms discrete packets dispersed in a matrix of another polymer is said to be heterogeneous in the solid state. Also a heterogeneous blend is defined to include co-continuous blends where the blend components are separately visible, but it is unclear which is the continuous phase and which is the discontinuous phase. Such morphology is determined using scanning electron microscopy (SEM) or atomic force microscopy (AFM). In the event the SEM and AFM provide different data, then the AFM data are used. By continuous phase is meant the matrix phase in a heterogeneous blend. By discontinuous phase is meant the dispersed phase in a heterogeneous blend.

The homogeneous polymer blend of the invention comprises an “at least partially cross-linked polymer”. The cross-linked polymer is formed by in-situ reaction between a polyene and second polymers. The presence and amount of such partially cross-linked polymer in the blend can be determined by a solvent extraction process. In this process the direct product of the polymerization process, without undergoing any additional curing steps, is first contacted with cyclohexane at 25° C. for 48 hours to separate the soluble components of the blend and then the remaining solids are refluxed at the boiling temperature of xylene for 24 hours with xylene to isolate the “at least partially cross-linked polymer”. The “at least partially cross-linked polymer” is also referred to herein as “xylene insolubles”. Details of the solvent extraction procedure are given in the Examples.

As used herein the term “substantially free of processing oil” means that the relevant product contains little or no of the oil-based processing aids, such as extender oils, synthetic processing oils, oligomeric extenders, or a combination thereof, that are added to conventional polymer blends to control the rheological characteristics of the blends during dynamic vulcanization. Preferably the relevant product contains less than 1 weight % processing oil, more preferably less than 0.5 weight %, preferably less than 0.1 weight % processing oil. The amount of oil in the polymer blend is determined using solvent extraction as described later. By virtue of the fact that the second polymer of the polymer blend of the invention is formed as at least partially cross-linked particles dispersed in the first polymer phase in the polymerization reactor, the need for a subsequent dynamic vulcanization step and hence the need for addition of processing oil can be avoided. It is, however, to be appreciated that in some cases the polymer blend of the invention may be subjected to post-polymerization curing and/or vulcanization to produce additional cross-linking of the second polymer.

As used herein the term “curative” means any of the additives conventionally added to polymer blends to effect curing of one or more components of the blend during a post-polymerization, dynamic vulcanization step. Examples of known curatives include sulfur, sulfur donors, metal oxides, resin systems, such as phenolic resins, peroxide-based systems, hydrosilation with platinum or peroxide and the like, both with and without accelerators and coagents.

As used herein the term “bulky monomer” means an olefin monomer that is not a linear C₂ to C₂₀ alpha olefin. Bulky monomers include cyclic olefin monomers, such as 5-ethylidene-2-norbornadiene (ENB), 5-vinyl-2-norbornene (VNB) and cyclopentadiene; branched olefin monomers, such as 3,5,5 trimethyl hexene-1; and macromonomers, such as terminally unsaturated oligomers or terminally unsaturated polymers.

As used herein, the term “terminal unsaturation” is defined to mean vinyl unsaturation, vinylene unsaturation or vinylidene unsaturation, with vinyl unsaturation being preferred.

This invention relates to a homogeneous polymer blend comprising a semi-crystalline (at least 30% crystalline) thermoplastic first polymer and a second polymer different from, and less crystalline than, the first polymer, wherein the second polymer is produced by means of an in-situ cross-linking chemistry that takes place concurrently with the synthesis of the second polymer and conveniently in the same polymerization reaction zone. While not wishing to bound by theory, it is believed that reactive intermediates generated in the production of the first polymer engage in the polymerization processes taking place in the production of the second polymer, producing hybrid polymers (also known as branch-block copolymers) that combine the characteristics of the first and second reactor polymers, such as the melting temperature of the first polymer and the lower glass transition temperature of the second polymer.

This invention also relates to a process for making the above polymer blend. In a reactor, a semi-crystalline polymer is produced in a first polymerization step. In a second polymerization step, the elastomeric polymer is synthesized, in the presence of the semi-crystalline polymer. It is believed that the elastomer takes the form of a fine particle dispersion in the semi-crystalline phase. The elastomer is cross-linked through the use of multifunctional monomers, particularly a polyene having at least two polymerizable unsaturated groups, with the degree of crosslinking being controlled by the reaction environment during the polymerization.

Following the two polymerization steps, the product composition, direct from the polymerization reactor, can undergo a typical polymer finishing operation, where suitable additives are incorporated and the polymer is melt homogenized. The finished product displays easy processability, high scratch resistance, high elastic recovery, high tensile strength and elongation. Heretofore, such properties were only possible via dynamic vulcanization.

The First Polymer

The first polymer of the homogeneous polymer blend of the present invention may be any crystalline or semi-crystalline thermoplastic polymer or a mixture thereof. Useful thermoplastic polymers have a crystallinity of at least 30%, more preferably at least 40% as determined by differential scanning calorimetry (DSC). The first polymer provides the composition with required tensile strength and temperature resistance. Accordingly, semi-crystalline polymers with a melting temperature, as measured by DSC, at or above 100° C., preferably above 120° C., preferably above 140° C., for example from 100 to 170° C., are desired. Typically, the first polymer has a crystallization temperature (Tc) between about 20 and about 120° C., such as between about 70 and about 110° C. preferably, the first polymer has a melt flow rate (MFR) of 2000 dg/min or less, such as 100 dg/min or less. Polymers with a high glass transition temperature to provide elevated temperature resistance are also acceptable as the thermoplastic first polymer.

Exemplary thermoplastic polymers for use as the first polymer include the family of polyolefin resins, polyesters (such as polyethylene terephthalate, polybutylene terephthalate), polyamides (such as nylons), polycarbonates, styrene-acrylonitrile copolymers, polystyrene, polystyrene derivatives, polyphenylene oxide, polyoxymethylene, and fluorine-containing thermoplastics. The preferred thermoplastic resins are crystallizable polyolefins that are formed by polymerizing C₂ to C₂₀ olefins such as, but not limited to, ethylene, propylene and C₄ to C₁₂ α-olefins, such as 1-butene, 1-hexene, 1-octene, 2-methyl-1-propene, 3-methyl-1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene, and mixtures thereof. Copolymers of ethylene and propylene or ethylene or propylene with another α-olefin, such as butene-1; pentene-1,2-methylpentene-1,3-methylbutene-1; hexene-1,3-methylpentene-1,4-methylpentene-1,3,3-dimethylbutene-1; heptene-1; hexene-1; methylhexene-1; dimethylpentene-1 trimethylbutene-1; ethylpentene-1; octene-1; methylpentene-1; dimethylhexene-1; trimethylpentene-1; ethylhexene-1; methylethylpentene-1; diethylbutene-1; propylpentane-1; decene-1; methylnonene-1; nonene-1; dimethyloctene-1; trimethylheptene-1; ethyloctene-1; methylethylbutene-1; diethylhexene-1 and dodecene-1, may also be used.

In one embodiment, the thermoplastic first polymer comprises a propylene homopolymer, a copolymer of propylene, or a mixture of propylene homopolymers and copolymers. Typically, the propylene polymer is predominately crystalline, i.e., it has a melting point generally greater than 110° C., alternatively greater than 115° C., and preferably greater than 130° C. The term “crystalline,” as used herein, characterizes those polymers that possess high degrees of inter- and intra-molecular order in the solid state. Heat of fusion, a measure of crystallinity, greater than 60 J/g, alternatively at least 70 J/g, alternatively at least 80 J/g, as determined by DSC analysis, is preferred. The heat of fusion is dependent on the composition of the polypropylene. A propylene homopolymer will have a higher heat of fusion than a copolymer or blend of a homopolymer and copolymer.

Where the thermoplastic first polymer is polypropylene, the polymer can vary widely in composition. For example, substantially isotactic polypropylene homopolymer or propylene copolymer containing 10 weight percent or less, preferably 5 weight percent or less, of an alpha-olefin comonomer can be used (i.e., at least 90% by weight propylene). Further, polypropylene segments may be part of graft or block copolymers having a sharp melting point above 110° C. and alternatively above 115° C. and alternatively above 130° C., characteristic of the stereoregular propylene sequences. The first polymer may be a combination of homopolypropylene, and/or random, and/or block copolymers as described herein. When the first polymer is a random copolymer, the percentage of the copolymerized alpha-olefin in the copolymer is, in general, up to 9% by weight, alternatively 0.5% to 8% by weight, alternatively 2% to 6% by weight. The preferred alpha-olefins contain 2 or from 4 to 12 carbon atoms. One, two or more alpha-olefins can be copolymerized with propylene.

The Second Polymer

The second polymer of the homogeneous polymer blend of the invention is generally an elastomeric polymer or copolymer and is polymerized and also cross-linked in the presence of the first polymer. The second polymer can include any polymer, copolymer, or mixture thereof that is capable of forming a cross-linked system during polymerization. Generally, the second polymer is produced by polymerizing a monomer mixture comprising at least 15 wt % of at least one C₃ to C₂₀ alpha-olefin and at least 0.0001 wt % of a polyene.

The second polymer has a crystallinity of at least 5%, such as from 10 to 50%, preferably from 10 to 45%, preferably from 10 to 40%, preferably from 10 to 35%. Generally, the second polymer has a lower crystallinity than that of the first polymer, although typically the crystallinity difference between the first polymer and the second polymer is less than 20%. Percent crystallinity is determined according to the DSC procedure described above.

The level of crystallinity is also reflected in the melting point. The term “melting point,” as used herein, for the second polymer component, is the highest temperature peak among principal and secondary melting peaks as determined by DSC, discussed above. In one embodiment of the present invention, the polymer has a single melting point. Typically, a sample of propylene copolymer will show secondary melting peaks adjacent to the principal peak, which are considered together as a single melting point. The highest of these peaks is considered the melting point. The second polymer preferably has a melting point by DSC ranging from an upper limit of 110° C., 105° C., 90° C., 80° C., or 70° C., to a lower limit of 20° C., 25° C., 30° C., 35° C., 40° C., or 45° C.

Suitable elastomeric copolymers for use as the second polymer component of the present homogeneous blend are semi-crystalline copolymers produced by copolymerizing two or more alpha olefins with at least one polyene, normally a diene. More typically, the elastomeric component is a copolymer of ethylene with at least one alpha-olefin monomer, and at least one diene monomer. The alpha-olefins may include, but are not limited to, C₃ to C₂₀ alpha-olefins, such as propylene, butene-1, hexene-1,4-methyl-1 pentene, octene-1, decene-1, or combinations thereof. The preferred alpha-olefins are propylene, hexene-1, octene-1 or combinations thereof. Thus, for example, the second polymer can be an ethylene-propylene-diene terpolymer.

Generally, olefins are present in the elastomeric second polymer component of the homogeneous polymer blend of the invention at levels from about 95 to about 99.99 wt %, whereas the diene content of the elastomeric copolymer is from about 0.01 wt % to about 5 wt %. Some embodiments have two or more different olefin units in the elastomeric component, with at least one olefin unit being selected from ethylene, propylene and C₄ to C₂₀ alpha-olefins. Typically, said at least one olefin unit comprises ethylene and a further olefin unit is selected from propylene and C₄ to C₁₂ alpha-olefins, especially propylene. These embodiments typically have one olefin present in amounts of from 12 to 98 wt %, for example from 30 to 95 wt %, of the copolymer whereas the other olefin is present in amounts of from 2 to 88 wt %, for example from 2 to 30 wt %, of the copolymer.

Still more desirably, the copolymer includes ethylene units in the range from 2 wt % to 88 wt % of the copolymer; propylene or other α-olefin(s) units in the range from 98 wt % to 12 wt %, desirably ethylene units in the range from 5 to 20 wt % and propylene or other α-olefin(s) units in the range from 95 to 80 wt %; more desirably ethylene units in the range from 5 wt % to 15 wt % and propylene or other α-olefin(s) units in the range from 95 to 85 wt % of the copolymer.

In another embodiment, the second polymers component includes a homopolymer or random copolymer of propylene having a heat of fusion as determined by Differential Scanning calorimetry (DSC) of less than 75 J/g, a MFR of 1500 dg/min or less, and contains stereoregular propylene crystallinity, preferably isotactic stereoregular propylene crystallinity. For example, the polymer can be a random copolymer of propylene and about 2 to about 15 wt % of at least one comonomer selected from ethylene, C₄-C₁₂ α-olefins, and combinations thereof, based on the total weight of the polymer. Preferably the random copolymer of propylene comprises from 5 wt % to 12 wt % polymerized ethylene units, based on the total weight of the polymer; has a narrow intermolecular composition distribution (e.g. 75% or more); has a melting point (Tm) of from 25° C. to 130° C., or from 35° C. to 100° C.; has a heat of fusion within the range having an upper limit of 75 J/g and a lower limit of 10 J/g.

A particularly preferred polymer useful as the second polymer component is a polymer with a moderate level of crystallinity due to stereoregular propylene sequences. The polymer can be (A) a propylene homopolymer in which the stereoregularity is disrupted in some manner such as by regio-inversions; (B) a random propylene copolymer in which the propylene stereoregularity is disrupted at least in part by comonomer incorporation; or (C) a combination of (A) and (B).

The second polymer component is polymerized and also cross-linked in the presence of the first polymer, normally by virtue of the presence of a polyene in the monomer combination used to produce the second polymer. In one embodiment, the polyene has at least two unsaturated bonds that can readily be incorporated into polymers to form cross-linked polymers. Examples of such polyenes include α,ω-dienes (such as butadiene, 1,4-pentadiene, 1,5-hexadiene, 1,6-heptadiene, 1,7-octadiene, 1,8-nonadiene, 1,9-decadiene, 1,10-undecadiene, 1,11-dodecadiene, 1,12-tridecadiene, and 1,13-tetradecadiene) and certain multi-ring alicyclic fused and bridged ring dienes (such as tetrahydroindene; norborndiene; methyl-tetrahydroindene; dicyclopentadiene; bicyclo-(2.2.1)-hepta-2,5-diene; and alkenyl-, alkylidene-, cycloalkenyl-, and cylcoalkylene norbornenes [including, e.g., 5-methylene-2-norbornene, 5-ethylidene-2-norbornene, 5-propenyl-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene, 5-cyclohexylidene-2-norbornene, and 5-vinyl-2-norbornene]).

In further embodiment, the polyene has at least two unsaturated bonds wherein one of the unsaturated bonds is readily incorporated into a polymer. The second bond may partially take part in polymerization to form cross-linked polymers but normally provides at least some unsaturated bonds in the polymer product suitable for subsequent functionalization (such as with maleic acid or maleic anhydride), curing or vulcanization or other chemical modification in post polymerization processes. Examples of polyenes according to said further embodiment include, but are not limited to butadiene, pentadiene, hexadiene, heptadiene, octadiene, nonadiene, decadiene, undecadiene, dodecadiene, tridecadiene, tetradecadiene, pentadecadiene, hexadecadiene, heptadecadiene, octadecadiene, nonadecadiene, icosadiene, heneicosadiene, docosadiene, tricosadiene, tetracosadiene, pentacosadiene, hexacosadiene, heptacosadiene, octacosadiene, nonacosadiene, triacontadiene, and polybutadienes having a molecular weight (M_(w)) of less than 1000 g/mol. Examples of straight chain acyclic dienes include, but are not limited to 1,4-hexadiene and 1,6-octadiene. Examples of branched chain acyclic dienes include, but are not limited to 5-methyl-1,4-hexadiene, 3,7-dimethyl-1,6-octadiene, and 3,7-dimethyl-1,7-octadiene. Examples of single ring alicyclic dienes include, but are not limited to 1,4-cyclohexadiene, 1,5-cyclooctadiene, and 1,7-cyclododecadiene. Examples of multi-ring alicyclic fused and bridged ring dienes include, but are not limited to tetrahydroindene; norbornadiene; methyl-tetrahydroindene; dicyclopentadiene; bicyclo-(2.2.1)-hepta-2,5-diene; and alkenyl-, alkylidene-, cycloalkenyl-, and cylcoalkyliene norbornenes [including, e.g., 5-methylene-2-norbornene, 5-ethylidene-2-norbornene, 5-propenyl-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene, 5-cyclohexylidene-2-norbornene, and 5-vinyl-2-norbornene]. Examples of cycloalkenyl-substituted alkenes include, but are not limited to vinyl cyclohexene, allyl cyclohexene, vinyl cyclooctene, 4-vinyl cyclohexene, allyl cyclodecene, vinyl cyclododecene, and tetracyclo (A-11,12)-5,8-dodecene.

According to one aspect of the invention, during the second polymerization step to produce the elastomeric component, it is believed that a distribution of cross-products are formed emanating principally from the grafting of the first thermoplastic polymer to the second elastomeric polymer. These hybrid cross-products, also known as branch-block copolymers, form when reactive intermediates from the first polymerization step cross-over into the second polymerization step and participate in the polymerization of the second polymer. The presence of branch-block copolymers is believed to influence the events occurring during the polymerization as well as product properties. The extent of influence depends on the population distribution of the branch-block copolymer fraction.

The amount of second polymer relative to the first polymer may vary widely depending on the nature of the polymers and the intended use of the final polymer blend. In particular, however, one advantage of the process of the invention is the ability to be able to produce a homogeneous polymer blend in which the second polymer comprises more than 50 wt %, such as more than 60 wt %, for example more than 70 wt % of the total homogeneous polymer blend. For TPV applications, the weight ratio of the second polymer to the first polymer is generally from about 90:10 to about 50:50, more preferably from about 80:20 to about 60:40, and most preferably from about 75:25 to about 65:35. For TPO or impact copolymer applications, the weight ratio of the second polymer to the first polymer is generally from about 49:51 to about 10:90, more preferably from 35:65 to about 15:85.

Production of the Polymer Blend

According to the invention, the polymer composition is produced by a novel two-step process. In the first step, a crystalline thermoplastic polymer is produced by polymerizing at least one first monomer in one or more polymerization zones. The effluent from the first step is then fed into a second polymerization step where an elastomer is produced in the presence of the polymer produced in the first step. The elastomer is in-situ cross-linked, at least partially, in the second polymerization zone. It is believed that the cross-linked elastomer forms finely dispersed particles embedded within the crystalline thermoplastic matrix, even though the blend forms a homogeneous phase morphology.

In an alternative embodiment, the first step of polymerization is replaced with addition of pre-made crystalline thermoplastic polymer. The pre-made polymer can be produced in a separate system or can be a commercially available product. The crystalline thermoplastic polymer can be dissolved in a solvent and then added into a reaction medium for the second polymerization step. The crystalline thermoplastic polymer can be also ground into fine powder and then added into the reaction medium for the second polymerization step.

Any known polymerization process may be used to produce the first thermoplastic polymer. For example, the polymer may be a propylene homopolymer obtained by homopolymerization of propylene in a single stage or multiple stage reactor. Copolymers may be obtained by copolymerizing propylene and an alpha-olefin having 2 or from 4 to 20 carbon atoms in a single stage or multiple stage reactor. Polymerization methods include high pressure, slurry, gas, bulk, suspension, supercritical, or solution phase, or a combination thereof, using a traditional Ziegler-Natta catalyst or a single-site metallocene catalyst system, or combinations thereof including bimetallic (i.e, Z/N and/or metallocene) catalysts. Preferred catalysts are those capable of polymerizing a C₂ to C₂₀ olefin to produce a first polymer having at least 30% crystallinity and at least 0.01% terminal unsaturation. The catalysts can be in the form of a homogeneous solution, supported, or a combination thereof. Polymerization may be carried out by a continuous, a semi-continuous or batch process and may include use of chain transfer agents, scavengers, or other such additives as deemed applicable. By continuous is meant a system that operates (or is intended to operate) without interruption or cessation. For example a continuous process to produce a polymer would be one where the reactants are continually introduced into one or more reactors and polymer product is continually withdrawn.

Where the thermoplastic polymer comprises a polyolefin, such as a propylene polymer or copolymer, the polyolefin will generally be produced in the presence of a single site catalyst, preferably a metallocene catalyst, with an activator and optional scavenger. Preferred metallocene catalysts are those in the generic class of bridged, substituted bis(cyclopentadienyl) metallocenes, specifically bridged, substituted bis(indenyl) metallocenes known to produce high molecular weight, high melting, highly isotactic propylene polymers. Particularly suitable catalysts are bridged bis-indenyl metallocene catalysts having a substituent on one or both of the 2- and 4-positions on each indenyl ring or those having a substituent on the 2-, 4-, and 7-positions on each indenyl ring. Generally speaking, those of the generic class disclosed in U.S. Pat. No. 5,770,753 (fully incorporated herein by reference) should be suitable, however, it has been found that the exact polymer obtained is dependent on the metallocene's specific substitution pattern, among other things. A specific list of useful catalyst compounds is found in International Patent Publication No. WO 2004/026921 at page 29 paragraph [00100] to page 66, line 4. In another embodiment, the catalyst compounds described in International Patent Publication No. WO 2004/026921 at page 66, paragraph [00103] to page 70, line 3 may also be used in the practice of this invention.

Particularly preferred are racemic metallocenes, such as rac-dimethylsiladiyl(2-isopropyl,4-phenylindenyl)₂ zirconium dichloride; rac-dimethylsiladiyl(2-isopropyl,4-[1-naphthyl]indenyl)₂ zirconium dichloride; rac-dimethylsiladiyl(2-isopropyl,4-[3,5-dimethylphenyl]indenyl)₂ zirconium dichloride; rac-dimethylsiladiyl(2-isopropyl,4-[ortho-methyl-phenyl]indenyl)₂ zirconium dichloride; rac-dimethylsilyl bis-(2-methyl, 4-phenylindenyl)zirconium dichloride, rac dimethylsiladlyl bis-(2-methyl, 4-napthylindenyl)zirconium dichloride, rac-dimethyl siladiyl(2-isopropyl, 4-[3,5 di-t-butyl-phenyl]indenyl)₂ zirconium dichloride; rac-dimethyl siladiyl(2-isopropyl, 4-[orthophenyl-phenyl]indenyl)₂ zirconium dichloride, rac-diphenylsiladiyl(2-methyl-4-[1-naphthyl]indenyl)₂ zirconium dichloride and rac-biphenyl siladiyl(2-isopropyl, 4-[3,5 di-t-butyl-phenyl]indenyl)₂ zirconium dichloride. Alkylated variants of these metallocenes (e.g. di-methyl instead of dichloride) are also useful, particularly when combined with a non-coordinating anion type activator. These and other metallocene compositions are described in detail in U.S. Pat. Nos. 6,376,407, 6,376,408, 6,376,409, 6,376,410, 6,376,411, 6,376,412, 6,376,413, 6,376,627, 6,380,120, 6,380,121, 6,380,122, 6,380,123, 6,380,124, 6,380,330, 6,380,331, 6,380,334, 6,399,723 and 6,825,372.

The manner of activation of the catalyst used in the first polymerization step can vary. Alumoxane and preferably methyl alumoxane (MAO) can be used. Non-or weakly coordinating anion activators (NCA) may be obtained in any of the ways described in EP277004, EP426637. Activation generally is believed to involve abstraction of an anionic group such as the methyl group to form a metallocene cation, although according to some literature zwitterions may be produced. The NCA precursor can be an ion pair of a borate or aluminate in which the precursor cation is eliminated upon activation in some manner, e.g. trityl or ammonium derivatives of tetrakis pentafluorophenyl boron (See EP277004). The NCA precursor can be a neutral compound such as a borane, which is formed into a cation by the abstraction of and incorporation of the anionic group abstracted from the metallocene (See EP426638).

The alumoxane activator may be utilized in an amount to provide a molar aluminum to metallocene ratio of from 1:1 to 20,000:1 or more. The non-coordinating compatible anion activator may be utilized in an amount to provide a molar ratio of metallocene compound to non-coordinating anion of 10:1 to 1:1.

Particularly useful activators include dimethylaniliniumtetrakis(pentafluorophenyl)borate and dimethyl anilinium tetrakis(heptafluoro-2-naphthyl)borate. For a more detailed description of useful activators see International Patent Publication No. WO 2004/026921 at page 72, paragraph [00119] to page 81 paragraph [00151]. A list of particularly useful activators that can be used in the practice of this invention may be found at page 72, paragraph [00177] to page 74, paragraph [00178] of International Patent Publication No. WO 2004/046214.

Preferably, the first polymerization step is conducted in a continuous, stirred tank reactor. Tubular reactors equipped with the hardware to introduce feeds, catalysts and cross-linking agents in staged manner can also be used. Generally, polymerization reactors are agitated (stirred) to reduce or avoid concentration gradients. Reaction environments include the case where the monomer(s) acts as diluent or solvent as well as the case where a liquid hydrocarbon is used as diluent or solvent. Preferred hydrocarbon liquids include both aliphatic and aromatic fluids such as desulphurized light virgin naphtha and alkanes, such as propane, isobutane, mixed butanes, hexane, pentane, isopentane, cyclohexane, isooctane, and octane. In an alternate embodiment a perfluorocarbon or hydrofluorocarbon is used as the solvent or diluent.

Suitable conditions for the first polymerization step include a temperature from about 50 to about 250° C., preferably from about 50 to about 150° C., more preferably from about 70 to about 150° C. and a pressure of 0.1 MPa or more, preferably 2 MPa or more. The upper pressure limit is not critically constrained but is typically 200 MPa or less, preferably, 120 MPa or less, except when operating in supercritical phase then the pressure and temperature are above the critical point of the reaction media in question (typically over 95° C. and 4.6 MPa for propylene polymerizations). For more information on running supercritical polymerizations, see International Patent Publication No. WO 2004/026921. Temperature control in the reactor is generally obtained by balancing the heat of polymerization with reactor cooling via reactor jackets or cooling coils, auto refrigeration, pre-chilled feeds, vaporization of liquid medium (diluent, monomers or solvent) or combinations of all three. Adiabatic reactors with pre-chilled feeds may also be used.

In the second polymerization step, some or all of the first polymer formed in the first polymerization step is contacted with at least one second monomer, typically ethylene and a C₃ to C₂₀ olefin, and at least one cross-linking agent, typically a diene, under conditions sufficient to polymerize the second monomer(s) to produce the second polymer and also cross-link said second polymer. As a result of the cross-linking that occurs with the second polymerization step, the product of the second polymerization step contains at least a fraction which is insoluble in xylene. Preferably, the amount of said xylene insoluble fraction, is at least 4 wt %, such as at least 10 wt %, such as at least 20 wt %, of the polymer blend (that is, of the total weight of the first and second polymers).

Any known polymerization process, including solution, suspension, slurry, supercritical and gas phase polymerization processes, and any known polymerization catalyst can be used to produce the second polymer component. Generally, the catalyst used to produce the second polymer component should be capable of polymerizing bulky monomers and also be capable of producing a polymer having an Mw of 20,000 or more and a crystallinity of more than 5%.

In one embodiment, the catalyst employed to produce the second polymer component is the same as, or is compatible with, the catalyst used to produce the thermoplastic polymer. In such a case, the first and second polymerization zones can be in a multiple-zone reactor, or separate, series-connected reactors, with the entire effluent from the first polymerization zone, including any active catalyst, being transferred to the second polymerization zone. Additional catalyst can then be added, as necessary to the second polymerization zone. In a particularly preferred embodiment, the process of the invention is conducted in two or more series-connected, continuous flow, stirred tank or tubular reactors using metallocene catalysts.

In another embodiment, catalyst quenching is applied between the two polymerization zones and a separate catalyst is introduced in the second reaction zone to produce the elastomer component. Catalyst quenching agents (such as air or an alcohol) may be introduced into the effluent from the first polymerization zone right after the reactor exit to deactivate the catalyst used for the first polymerization. Scavenger may be useful and can be fed into the effluent downstream of the catalyst quenching agent injection point or the second polymerization zone.

Where a separate catalyst is used to produce the elastomeric second polymer, this is conveniently one of, or a mixture of, metallocene compounds of either or both of the following types:

-   -   1) Cyclopentadienyl (Cp) complexes which have two Cp ring         systems for ligands. The Cp ligands form a sandwich complex with         the metal and can be free to rotate (unbridged) or locked into a         rigid configuration through a bridging group. The Cp ring         ligands can be like or unlike, unsubstituted, substituted, or a         derivative thereof such as a heterocyclic ring system which may         be substituted, and the substitutions can be fused to form other         saturated or unsaturated rings systems such as         tetrahydroindenyl, indenyl, or fluorenyl ring systems. These         cyclopentadienyl complexes are represented by the formula

(Cp¹R¹ _(m))R³ _(n)(Cp²R² _(p))MX_(q)

-   -   wherein Cp¹ of ligand (Cp¹R¹ _(m)) and Cp² of ligand (Cp²R²         _(p)) are the same or different cyclopentadienyl rings, R¹ and         R² each is, independently, a halogen or a hydrocarbyl,         halocarbyl, hydrocarbyl-substituted organometalloid or         halocarbyl-substituted organometalloid group containing up to         about 20 carbon atoms, m is 0, 1, 2, 3, 4, or 5, p is 0, 1, 2,         3, 4 or 5, and two R¹ and/or R² substituents on adjacent carbon         atoms of the cyclopentadienyl ring associated there with can be         joined together to form a ring containing from 4 to about 20         carbon atoms, R³ is a bridging group, n is the number of atoms         in the direct chain between the two ligands and is 0, 1, 2, 3,         4, 5, 6, 7, or 8, preferably 0, 1, 2, or 3, M is a transition         metal having a valence of 3, 4, 5 or 6, preferably from Group 4,         5, or 6 of the Periodic Table of the Elements and is preferably         in its highest oxidation state, each X is a non-cyclopentadienyl         ligand and is, independently, a halogen or a hydrocarbyl,         oxyhydrocarbyl, halocarbyl, hydrocarbyl-substituted         organometalloid, oxyhydrocarbyl-substituted organometalloid or         halocarbyl-substituted organometalloid group containing up to         about 20 carbon atoms, q is equal to the valence of M minus 2.     -   2) Monocyclopentadienyl complexes which have only one Cp ring         system as a ligand. The Cp ligand forms a half-sandwich complex         with the metal and can be free to rotate (unbridged) or locked         into a rigid configuration through a bridging group to a         heteroatom-containing ligand. The Cp ring ligand can be         unsubstituted, substituted, or a derivative thereof such as a         heterocyclic ring system which may be substituted, and the         substitutions can be fused to form other saturated or         unsaturated rings systems such as tetrahydroindenyl, indenyl, or         fluorenyl ring systems. The heteroatom containing ligand is         bound to both the metal and optionally to the Cp ligand through         the bridging group. The heteroatom itself is an atom with a         coordination number of three from Group 15 or 16 of the periodic         table of the elements. These mono-cyclopentadienyl complexes are         represented by the formula

(Cp¹R¹ _(m))R³ _(n)(YR²)MX_(s)

-   -   wherein R¹ is, each independently, a halogen or a hydrocarbyl,         halocarbyl, hydrocarbyl-substituted organometalloid or         halocarbyl-substituted organometalloid group containing up to         about 20 carbon atoms, m is 0, 1, 2, 3, 4 or 5, and two R¹         substituents on adjacent carbon atoms of the cyclopentadienyl         ring associated therewith can be joined together to form a ring         containing from 4 to about 20 carbon atoms, R³ is a bridging         group, n is 0, or 1, M is a transition metal having a valence of         from 3, 4, 5, or 6, preferably from Group 4, 5, or 6 of the         Periodic Table of the Elements and is preferably in its highest         oxidation state, Y is a heteroatom containing group in which the         heteroatom is an element with a coordination number of three         from Group 15 or a coordination number of two from Group 16         preferably nitrogen, phosphorous, oxygen, or sulfur, R² is a         radical independently selected from a group consisting of C₁ to         C₂₀ hydrocarbon radicals, substituted C₁ to C₂₀ hydrocarbon         radicals, wherein one or more hydrogen atoms is replaced with a         halogen atom, and when Y is three coordinate and unbridged there         may be two R₂ groups on Y each independently a radical selected         from a group consisting of C₁ to C₂₀ hydrocarbon radicals,         substituted C₁ to C₂₀ hydrocarbon radicals, wherein one or more         hydrogen atoms is replaced with a halogen atom, and each X is a         non-cyclopentadienyl ligand and is, independently, a halogen or         a hydrocarbyl, oxyhydrocarbyl, halocarbyl,         hydrocarbyl-substituted organometalloid,         oxyhydrocarbyl-substituted organometalloid or         halocarbyl-substituted organometalloid group containing up to         about 20 carbon atoms, s is equal to the valence of M minus 2;         Cp¹ is a Cp ring.

Examples of suitable biscyclopentadienyl metallocenes of the type described in Group 1 above for the invention are disclosed in U.S. Pat. Nos. 5,324,800; 5,198,401; 5,278,119; 5,387,568; 5,120,867; 5,017,714; 4,871,705; 4,542,199; 4,752,597; 5,132,262; 5,391,629; 5,243,001; 5,278,264; 5,296,434; and 5,304,614, all of which are incorporated by reference herein.

Illustrative, but not limiting examples of preferred biscyclopentadienyl metallocenes of the type described in Group 1 above for the invention are the racemic isomers of:

μ-(CH₃)₂Si(indenyl)₂M(Cl)₂

μ-(CH₃)₂Si(indenyl)₂M(CH₃)₂

μ-(CH₃)₂Si(tetrahydroindenyl)₂M(Cl)₂

μ-(CH₃)₂Si(tetrahydroindenyl)₂M(CH₃)₂

μ-(CH₃)₂Si(indenyl)₂M(CH₂CH₃)₂

μ-(C₆H₅)₂C(indenyl)₂M(CH₃)₂

wherein M is chosen from a group consisting of Zr and Hf

Examples of suitable unsymmetrical cyclopentadienyl metallocenes of the type described in Group 1 above for the invention are disclosed in U.S. Pat. Nos. 4,892,851; 5,334,677; 5,416,228; and 5,449,651; and are described in publication J Am. Chem. Soc. 1988, 110, 6255, all of which are incorporated by reference herein.

Illustrative, but not limiting examples of preferred unsymmetrical cyclopentadienyl metallocenes of the type described in Group 1 above for the invention are:

μ-(C₆H₅)₂C(cyclopentadienyl)(fluorenyl)M(R)₂

μ-(C₆H₅)₂C(3-methylcyclopentadienyl)(fluorenyl)M(R)₂

μ-(CH₃)₂C(cyclopentadienyl)(fluorenyl)M(R)₂

μ-(C₆H₅)₂C(cyclopentadienyl)(2-methylindenyl)M(R)₂

μ-(C₆H₅)₂C(3-methylcyclopentadienyl)(2-methylindenyl)M(R)₂

μ-(p-triethylsilylphenyl)₂C(cyclopentadienyl)(3,8-di-t-butylfluorenyl)M(R)₂

μ-(C₆H₅)₂C(cyclopentadienyl)(2,7-dimethylindenyl)M(R)₂

μ-(CH₃)₂C(cyclopentadienyl)(2,7-dimethylindenyl)M(R)₂.

wherein M is chosen from the group consisting of Zr and Hf and R is chosen from the group consisting of C₁ and CH₃.

Examples of suitable monocyclopentadienyl metallocenes of the type described in group 2 above for the invention are disclosed in U.S. Pat. Nos. 5,026,798; 5,057,475; 5,350,723; 5,264,405; and 5,055,438 and International Patent Publication No. WO 96/002244, all of which are incorporated by reference herein.

Illustrative, but not limiting examples of preferred monocyclopentadienyl metallocenes of the type described in group 2 above for the invention are:

μ-(CH₃)₂Si(cyclopentadienyl)(1-adamantylamido)M(R)₂

μ-(CH₃)₂Si(3-tertbutylcyclopentadienyl)(1-adamantylamido)M(R)₂

μ-(CH₃)₂Si(tetramethylcyclopentadienyl)(1-adamantylamido)M(R)₂

μ-(CH₃)₂C(tetramethylcyclopentadienyl)(1-adamantylamido)M(R)₂

μ-(CH₃)₂Si(tetramethylcyclopentadienyl)(1-tertbutylamido)M(R)₂

μ-(CH₃)₂Si(fluorenyl)(1-tertbutylamido)M(R)₂

μ-(CH₃)₂Si(tetramethylcyclopentadienyl)(1-cyclododecylamido)M(R)₂

μ-(CH₃)₂C(tetramethylcyclopentadienyl)(1-cyclododecylamido)M(R)₂

wherein M is selected from a group consisting of Ti, Zr, and Hf and wherein R is selected from Cl and CH₃.

Another class of organometallic complexes that are useful catalysts for producing the second polymer component are those with diimido ligand systems such as those described in International Patent Publication No. WO 96/23010. These catalytic polymerization compounds are incorporated here by reference.

In a preferred processing mode, the conditions in the second polymerization zone are arranged not only to copolymerize the elastomer monomers with the bifunctional monomer, such as a diene, but also to cause at least partial cross-linking of resultant elastomer. Typical conditions in the second polymerization zone include a temperature of about 10° C. to about 250° C. and a pressure of about 0.1 MPa to about 200 MPa.

The second polymer, which is at least partially cross-linked in the copolymerization reaction of olefins and dienes, may be prepared by solution, suspension or slurry polymerization of the olefins and diene under conditions in which the catalyst site remains relatively insoluble and/or immobile so that the polymer chains are rapidly immobilized following their formation. Such immobilization is affected, for example, by (1) using a solid, insoluble catalyst, (2) maintaining the polymerization below the crystalline melting point of thermoplastic polymers made in the first step and (3) using low solvency solvent such as a fluorinated hydrocarbon.

In a solution process, the uncrosslinked second polymers are preferably dissolved (or are soluble) in the polymerization media. The second polymers are then phase separated from the reaction media to form micro-particles when the polymers are cross-linked. This in-situ cross-link and phase separation facilitates the process to produce polymers of high molecular weight.

By selecting the catalyst systems (i.e., catalyst and activator), the polymerization reaction conditions, and/or by introducing a diene modifier, some molecules of the first polymer(s) and the second polymer(s) can be linked together to produce branch-block structures. While not wishing to be bound by theory, the branch-block copolymer is believed to comprise a low crystalline polymer backbone having crystalline side chains originating from the first polymer.

To effectively incorporate the polymer chains of the first polymer into the growing chains of the second polymer, it is preferable that the first polymerization step produces macromonomers having reactive termini, such as vinyl end groups. By macromonomers having reactive termini is meant a polymer having twelve or more carbon atoms (preferably 20 or more, more preferably 30 or more, more preferably between 12 and 8000 carbon atoms) and having a vinyl, vinylidene, vinylene or other terminal group that can be polymerized into a growing polymer chain. By capable of polymerizing macromonomer having reactive termini is meant a catalyst component that can incorporate a macromonomer, having reactive termini into a growing polymer chain. Vinyl terminated chains are generally more reactive than vinylene or vinylidene terminated chains. Generally, it is desirable that the first polymerization step produces a first polymer having at least 0.01% terminal unsaturation.

Optionally the thermoplastic first polymers are copolymers of one or more alpha olefins and one or more of monomers having at least two olefinically unsaturated bonds. Both of these unsaturated bonds are suitable for and readily incorporated into a growing polymer chain by coordination polymerization using either the first or second catalyst systems independently such that one double bond is incorporated into the first polymer segments while another double bond is incorporated into the second elastomeric polymer segments to form a branched block copolymer. In a preferred embodiment these monomers having at least two olefinically unsaturated bonds are di-olefins, preferably di-vinyl monomers.

A polymer can be recovered from the effluent of either the first polymerization step or the second polymerization step by separating the polymer from other constituents of the effluent using conventional separation means. For example, polymer can be recovered from either effluent by coagulation with a non-solvent such as isopropyl alcohol, acetone, or n-butyl alcohol, or the polymer can be recovered by stripping the solvent or other media with heat or steam. One or more conventional additives such as antioxidants can be incorporated in the polymer during the recovery procedure. Possible antioxidants include phenyl-beta-naphthylamine; di-tert-butylhydroquinone, triphenyl phosphate, heptylated diphenylamine, 2,2′-methylene-bis(4-methyl-6-tert-butyl)phenol, and 2,2,4-trimethyl-6-phenyl-1,2-dihydroquinoline. Other methods of recovery such as by the use of lower critical solution temperature (LCST) followed by devolatilization are also envisioned. The catalyst may be deactivated as part of the separation procedure to reduce or eliminate further uncontrolled polymerization downstream the polymer recovery processes. Deactivation may be effected by the mixing with suitable polar substances such as water, whose residual effect following recycle can be counteracted by suitable sieves or scavenging systems.

Properties of the Polymer Blend

The in-reactor produced homogeneous polymer blend, where the first semi-crystalline component is produced in the first polymerization zone and the polymerized product is transferred to the second reactor zone, where polymerization of the cross-linked second polymer occurs, comprises not only an intimate mix of the two polymer components but also at least a portion of the second phase is cross-linked and preferably comprises a hybrid species of said first and second polymers having characteristics of the first and second polymers such as a melting temperature, preferably of at least 100° C., in the xylene insoluble fraction.

In addition, since at least some cross-linking of the second polymer occurs during the second polymerization step, rather than all the cross-linking being effected in a subsequent dynamic extrusion step, the second polymer component of the homogeneous polymer blend of the invention comprises at least a fraction which is insoluble in xylene and which is substantially free of the curatives normally added to polymers blends to effect cross-linking during post-polymerization, dynamic extrusion. By substantially free is meant that the dispersed phase contains less than 1,000 ppm, such as less than 100 ppm, such as less than 10 ppm, of a curative.

Polymers with bimodal distributions of molecular weight and composition can be produced by the polymerization process of the invention, by, for example, controlling the polymerization conditions in the first and the second polymerization zones and selecting the catalysts for the first and the second polymerizations, such as by using multiple catalysts in each polymerization zone. Bimodal distributions of molecular weight and composition of the second polymer can also be obtained when different catalysts are used in the first and second polymerization zones and the catalyst employed in the first polymerization zone is transferred into the second polymerization zone for production of the cross-linked elastomer.

The individual components of the homogeneous polymer blend of the invention can readily be separated by solvent extraction. In a suitable solvent extraction regime, the blend, without undergoing any additional processing steps, is contacted with cyclohexane at 25° C. for 48 hours to separate the soluble components of the blend and then the remaining solids are refluxed at the boiling temperature of xylene for 24 hours with xylene to dissolve the thermoplastic phase material as well as branched elastomer. The remaining xylene insolubles comprise the cross-linked elastomer as well as hybrid copolymers of the first and second polymers. These hybrid copolymers typically exhibit a melting temperature in excess of 100° C.

In one embodiment, the polymer blend described herein has a tensile strength at break (as measured by ISO 37 at 23° C.) of 0.5 MPa or more, alternatively 0.75 MPa or more, alternatively 1.0 MPa or more, alternatively 1.5 MPa or more, alternatively 2.0 MPa or more, alternatively 2.5 MPa or more, alternatively 3.0 MPa or more, alternatively 3.5 MPa or more.

In another embodiment, the polymer blend described herein has a Shore hardness of 30 A to 90 D, preferably 15 A to 90 D (as measured by ISO 868).

In another embodiment, the polymer blend described herein has an ultimate elongation (as measured by ISO 37) of 20% or more, preferably 30% or more, more preferably 40% or more.

In another embodiment, the polymer blend described herein has a compression set (as measured by ISO 815A) of 90% or less, preferably 70% or less, more preferably 50% or less, more preferably 30% or less.

In another embodiment, the polymer blend described herein has a tension set (as measured by ISO 2285) of 100% or less, preferably 80% or less, more preferably 60% or less, more preferably 20% or less.

In another embodiment, the polymer blend described herein has an oil swell (as measured by ASTM D471) of 500% or less, preferably 250% or less, more preferably 100% or less.

Additives

The homogeneous polymer blend according to the invention may optionally contain reinforcing and non-reinforcing fillers, plasticizers, antioxidants, stabilizers, rubber processing oils, extender oils, lubricants, antiblocking agents, antistatic agents, waxes, foaming agents, pigments, flame retardants and other processing aids known in the rubber compounding art. Such additives may comprise up to about 70 weight percent, more preferably up to about 65 weight percent, of the total composition. Fillers and extenders which can be utilized include conventional inorganics such as calcium carbonate, clays, silica, talc, titanium dioxide, carbon black and the like. The rubber processing oils generally are paraffinic, naphthenic or aromatic oils derived from petroleum fractions. The oils are selected from those ordinarily used in conjunction with the specific rubber or rubber component present in the composition.

The additives such as fillers and oils can be introduced into the homogeneous polymer blend during the polymerization in either the first polymerization zone or the second polymerization zone. The additives can be added into the effluent from the second polymerization zone and are preferably added into the polymer blend after removal of solvent or diluent through melt blending.

Additional polymers can also be added to form blends. In one or more embodiments, the additional polymers include thermoplastic resins or thermoplastic elastomers. Exemplary thermoplastic resins include crystalline polyolefins. Also, suitable thermoplastic resins may include copolymers of polyolefins with styrene, such as a styrene-ethylene copolymer. In one or more embodiments, the thermoplastic resins are formed by polymerizing ethylene or α-olefins such as propylene, 1-butene, 1-hexene, 1-octene, 2-methyl-1-propene, 3-methyl-1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene, and mixtures thereof. Copolymers of ethylene and propylene and ethylene and propylene with another α-olefin such as 1-butene, 1-hexene, 1-octene, 2-methyl-1-propene, 3-methyl-1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene or mixtures thereof are also contemplated. Specifically included are the homo-polypropylene, impact, and random copolymers of propylene with ethylene or the higher α-olefins, described above, or with C₁₀-C₂₀ diolefins. Preferably, the homopolypropylene has a melting point of at least 130° C., for example at least 140° C. and preferably less than or equal to 170° C., a heat of fusion of at least 75 J/g, alternatively at least 80 J/g, as determined by DSC analysis, and weight average molecular weight (Mw) of at least 50,000, alternatively at least 100,000. Comonomer contents for these propylene copolymers will typically be from 1 to about 30% by weight of the polymer (See, for example, U.S. Pat. Nos. 6,268,438, 6,288,171, and 6,245,856. Copolymers available under the tradename VISTAMAXX™ (ExxonMobil) are specifically included. Blends or mixtures of two or more polyolefin thermoplastics such as described herein, or with other polymeric modifiers, are also suitable in accordance with this invention. These homopolymers and copolymers may be synthesized by using an appropriate polymerization technique known in the art such as, but not limited to, the conventional Ziegler-Natta type polymerizations, and catalysis employing single-site organometallic catalysts including, but not limited to, metallocene catalysts.

Although the present polymer blend undergoes at least partial cross-linking during the second polymerization step, the elastomeric second polymer component of the in-reactor product may contain unreacted pendant double bonds. The in-reactor product may therefore be subjected to a finishing operation in which the unreacted double bonds undergo post polymerization curing to increase the curing density of the rubber phase. The increased curing density results in an increase in the fraction of the blend that is insoluble in xylene. Preferably, following post polymerization curing, the fraction of the blend insoluble in xylene comprises at least 10%, such as at least 20%, such as at least 30% of the in-reactor produced polymer blend.

In one or more embodiments, the diene cross-linking can be selected such that any pendant double bonds left unreacted after the second polymerization step can undergo thermal cross-linking during the finishing operation thereby increasing the crosslink density of the second polymer component.

In one or more embodiments, during the finishing step crosslinking agents can be injected into the polymer finishing equipment to increase the cure density of the dispersed rubber phase. Exemplary curatives include phenolic resin cure systems, peroxide cure systems, and silicon-containing cure systems

In one or more embodiments, the phenolic resins include those disclosed in U.S. Pat. Nos. 2,972,600, 3,287,440, 5,952,425 and 6,437,030, and International Publication No. PCT/US04/30518, which are incorporated herein by reference for purpose of U.S. patent practice.

Phenolic resin curatives can be referred to as resole resins, and include those resins made by the condensation of alkyl substituted phenols or unsubstituted phenols with aldehydes, such as formaldehydes, in an alkaline medium or by condensation of bi-functional phenoldialcohols. The alkyl substituents of the alkyl substituted phenols may contain 1 to about 10 carbon atoms. Dimethylolphenols or phenolic resins, substituted in para-positions with alkyl groups containing 1 to about 10 carbon atoms are preferred. In one embodiment, a blend of octyl phenol and nonylphenol-formaldehyde resins are employed. The blend may include from about 25 to about 40% by weight octyl phenol and from about 75 to about 60% by weight nonylphenol (optionally from about 30 to about 35 weight percent octyl phenol and from about 70 to about 65 weight percent nonylphenol). In one embodiment, the blend includes about 33% by weight octylphenol-formaldehyde and about 67% by weight nonylphenol formaldehyde resin, where each of the octylphenol and nonylphenol include methylol groups. This blend can be solubilized in paraffinic oil at about 30% solids.

Useful phenolic resins may be obtained under the tradenames SP-1044, SP-1045 (Schenectady International; Schenectady, N.Y.), which are referred to as alkylphenol-formaldehyde resins. SP-1045 is believed to be an octylphenol-formaldehyde resin that contains methylol groups. The SP-1044 and SP-1045 resins are believed to be essentially free of halogen substituents or residual halogen compounds. By essentially free of halogen substituents, it is meant that the synthesis of the resin provides for a non-halogenated resin that may only contain trace amounts of halogen containing compounds.

In one or more embodiments, the phenolic resin can be used in combination with a halogen source, such as stannous chloride, and a metal oxide or reducing compound such as zinc oxide.

In one or more embodiments, useful peroxide curatives include organic peroxides. Examples of organic peroxides include, but are not limited to, di-tert-butyl peroxide, dicumyl peroxide, t-butylcumyl peroxide, α,α-bis(tert-butylperoxy)diisopropyl benzene, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane (DBPH), 1,1-di(tert-butylperoxy)-3,3,5-trimethyl cyclohexane, n-butyl-4-4-bis(tert-butylperoxy) valerate, benzoyl peroxide, lauroyl peroxide, dilauroyl peroxide, 2,5-dimethyl-2,5-di(tert-butylperoxy) hexyne-3, and mixtures thereof. Also, diaryl peroxides, ketone peroxides, peroxydicarbonates, peroxyesters, dialkyl peroxides, hydroperoxides, peroxyketals and mixtures thereof may be used. Useful peroxides and their methods of use in dynamic vulcanization of thermoplastic vulcanizates are disclosed in U.S. Pat. No. 5,656,693, which is incorporated herein by reference for purpose of U.S. patent practice.

In one or more embodiments, the peroxide curatives are employed in conjunction with a coagent. Examples of coagents include triallylcyanurate, triallyl isocyanurate, triallyl phosphate, sulfur, N-phenyl bis-maleamide, zinc diacrylate, zinc dimethacrylate, divinyl benzene, 1,2 polybutadiene, trimethylol propane trimethacrylate, tetramethylene glycol diacrylate, trifunctional acrylic ester, dipentaerythritolpentacrylate, polyfunctional acrylate, retarded cyclohexane dimethanol diacrylate ester, polyfunctional methacrylates, acrylate and methacrylate metal salts, oximer for e.g., quinone dioxime. In order to maximize the efficiency of peroxide/coagent crosslinking the mixing and dynamic vulcanization are preferably carried out in a nitrogen atmosphere.

In one or more embodiments, useful silicon-containing cure systems include silicon hydride compounds having at least two SiH groups. It is believed that these compounds react with carbon-carbon double bonds of unsaturated polymers in the presence of a hydrosilation catalyst. Silicon hydride compounds that are useful in practicing the present invention include, but are not limited to, methylhydrogen polysiloxanes, methylhydrogen dimethyl-siloxane copolymers, alkyl methyl polysiloxanes, bis(dimethylsilyl)alkanes, bis(dimethylsilyl)benzene, and mixtures thereof.

Useful catalysts for hydrosilation include, but are not limited to, peroxide catalysts and catalysts including transition metals of Group VIII. These metals include, but are not limited to, palladium, rhodium, and platinum, as well as complexes of these metals. For a further discussion of the use of hydrosilation to cure thermoplastic vulcanizates, reference can be made to U.S. Pat. No. 5,936,028, which is incorporated herein by reference for purpose of U.S. patent practice. In one or more embodiments, a silicon-containing curative can be employed to cure an elastomeric copolymer including units deriving from 5-vinyl-2-norbornene.

In one or more embodiments, curatives that are useful for curing the present homogeneous polymer blend include those described in U.S. Pat. Nos. 5,013,793, 5,100,947, 5,021,500, 4,978,714, and 4,810,752, each of which is incorporated herein by reference.

Uses of the Polymer Blends

The homogeneous polymer blends described herein may be shaped into desirable end use articles by any suitable means known in the art. They are particularly useful for making articles by blow molding, extrusion, injection molding, thermoforming, gas foaming, elasto-welding and compression molding techniques.

Thermoforming is a process of forming at least one pliable plastic sheet into a desired shape. An embodiment of a thermoforming sequence is described, however this should not be construed as limiting the thermoforming methods useful with the compositions of this invention. First, an extrudate film of the composition of this invention (and any other layers or materials) is placed on a shuttle rack to hold it during heating. The shuttle rack indexes into the oven which pre-heats the film before forming. Once the film is heated, the shuttle rack indexes back to the forming tool. The film is then vacuumed onto the forming tool to hold it in place and the forming tool is closed. The forming tool can be either “male” or “female” type tools. The tool stays closed to cool the film and the tool is then opened. The shaped laminate is then removed from the tool.

Thermoforming is accomplished by vacuum, positive air pressure, plug-assisted vacuum forming, or combinations and variations of these, once the sheet of material reaches thermoforming temperatures, typically of from 140° C. to 185° C. or higher. A pre-stretched bubble step is used, especially on large parts, to improve material distribution. In one embodiment, an articulating rack lifts the heated laminate towards a male forming tool, assisted by the application of a vacuum from orifices in the male forming tool. Once the laminate is firmly formed about the male forming tool, the thermoformed shaped laminate is then cooled, typically by blowers. Plug-assisted forming is generally used for small, deep drawn parts. Plug material, design, and timing can be critical to optimization of the process. Plugs made from insulating foam avoid premature quenching of the plastic. The plug shape is usually similar to the mold cavity, but smaller and without part detail. A round plug bottom will usually promote even material distribution and uniform side-wall thickness.

The shaped laminate is then cooled in the mold. Sufficient cooling to maintain a mold temperature of 30° C. to 65° C. is desirable. The part is below 90° C. to 100° C. before ejection in one embodiment. For the good behavior in thermoforming, the lowest melt flow rate polymers are desirable. The shaped laminate is then trimmed of excess laminate material.

Blow molding is another suitable forming means, which includes injection blow molding, multi-layer blow molding, extrusion blow molding, and stretch blow molding, and is especially suitable for substantially closed or hollow objects, such as, for example, gas tanks and other fluid containers. Blow molding is described in more detail in, for example, CONCISE ENCYCLOPEDIA OF POLYMER SCIENCE AND ENGINEERING 90-92 (Jacqueline I. Kroschwitz, ed., John Wiley & Sons 1990).

In yet another embodiment of the formation and shaping process, profile co-extrusion can be used. The profile co-extrusion process parameters are as above for the blow molding process, except the die temperatures (dual zone top and bottom) range from 150° C. to 235° C., the feed blocks are from 90° C. to 250° C., and the water cooling tank temperatures are from 10° C. to 40° C.

One embodiment of an injection molding process is described as follows. The shaped laminate is placed into the injection molding tool. The mold is closed and the substrate material is injected into the mold. The substrate material has a melt temperature between 200° C. and 300° C., such as between 215° C. and 250° C. and is injected into the mold at an injection speed of between 2 and 10 seconds. After injection, the material is packed or held at a predetermined time and pressure to make the part dimensionally and aesthetically correct. Typical time periods are from 5 to 25 seconds and pressures from 1,380 kPa to 10,400 kPa. The mold is cooled between 10° C. and 70° C. to cool the substrate. The temperature will depend on the desired gloss and appearance desired. Typical cooling time is from 10 to 30 seconds, depending on part on the thickness. Finally, the mold is opened and the shaped composite article ejected.

Likewise, molded articles may be fabricated by injecting molten polymer into a mold that shapes and solidifies the molten polymer into desirable geometry and thickness of molded articles. Sheet may be made either by extruding a substantially flat profile from a die, onto a chill roll, or alternatively by calendaring. Sheet will generally be considered to have a thickness of from 10 mils to 100 mils (254 μm to 2540 μm), although sheet may be substantially thicker. Tubing or pipe may be obtained by profile extrusion for uses in medical, potable water, land drainage applications or the like. The profile extrusion process involves the extrusion of molten polymer through a die. The extruded tubing or pipe is then solidified by chill water or cooling air into a continuous extruded articles. The tubing will generally be in the range of from 0.31 cm to 2.54 cm in outside diameter, and have a wall thickness of in the range of from 254 cm to 0.5 cm. The pipe will generally be in the range of from 2.54 cm to 254 cm in outside diameter, and have a wall thickness of in the range of from 0.5 cm to 15 cm. Sheet made from the products of an embodiment of a version of the present invention may be used to form containers. Such containers may be formed by thermoforming, solid phase pressure forming, stamping and other shaping techniques. Sheets may also be formed to cover floors or walls or other surfaces.

In an embodiment of the thermoforming process, the oven temperature is between 160° C. and 195° C., the time in the oven between 10 and 20 seconds, and the die temperature, typically a male die, between 10° C. and 71° C. The final thickness of the cooled (room temperature), shaped laminate is from 10 μm to 6000 μm in one embodiment, from 200 μm to 6000 μm in another embodiment, and from 250 μm to 3000 μm in yet another embodiment, and from 500 μm to 1550 μm in yet another embodiment, a desirable range being any combination of any upper thickness limit with any lower thickness limit.

In an embodiment of the injection molding process, wherein a substrate material is injection molded into a tool including the shaped laminate, the melt temperature of the substrate material is between 230° C. and 255° C. in one embodiment, and between 235° C. and 250° C. in another embodiment, the fill time from 2 to 10 seconds in one embodiment, from 2 to 8 seconds in another embodiment, and a tool temperature of from 25° C. to 65° C. in one embodiment, and from 27° C. and 60° C. in another embodiment. In a desirable embodiment, the substrate material is at a temperature that is hot enough to melt any tie-layer material or backing layer to achieve adhesion between the layers.

In yet another embodiment of the invention, the compositions of this invention may be secured to a substrate material using a blow molding operation. Blow molding is particularly useful in such applications as for making closed articles such as fuel tanks and other fluid containers, playground equipment, outdoor furniture and small enclosed structures. In one embodiment of this process, Compositions of this invention are extruded through a multi-layer head, followed by placement of the uncooled laminate into a parison in the mold. The mold, with either male or female patterns inside, is then closed and air is blown into the mold to form the part.

It will be understood by those skilled in the art that the steps outlined above may be varied, depending upon the desired result. For example, an extruded sheet of the compositions of this invention may be directly thermoformed or blow molded without cooling, thus skipping a cooling step. Other parameters may be varied as well in order to achieve a finished composite article having desirable features.

The thermoplastic elastomer blends of this invention are useful for making a variety of articles such as weather seals, hoses, belts, gaskets, moldings, boots, elastic fibers and like articles. Foamed end-use articles are also envisioned. More specifically, the blends of the invention are particularly useful for making vehicle parts, such as but not limited to, weather seals, brake parts including, but not limited to cups, coupling disks, diaphragm cups, boots such as constant velocity joints and rack and pinion joints, tubing, sealing gaskets, parts of hydraulically or pneumatically operated apparatus, o-rings, pistons, valves, valve seats, valve guides, and other elastomeric polymer based parts or elastomeric polymers combined with other materials such as metal, plastic combination materials which will be known to those of ordinary skill in the art. Also contemplated are transmission belts including V-belts, toothed belts with truncated ribs containing fabric faced V's, ground short fiber reinforced Vs or molded gum with short fiber flocked V's. The cross section of such belts and their number of ribs may vary with the final use of the belt, the type of market and the power to transmit. They also can be flat made of textile fabric reinforcement with frictioned outside faces. Vehicles contemplated where these parts will find application include, but are not limited to passenger autos, motorcycles, trucks, boats and other vehicular conveyances.

In another embodiment, this invention relates to:

1. A homogeneous polymer blend comprising:

-   -   (a) a thermoplastic first polymer having a crystallinity of at         least 30%; and     -   (b) a second polymer having a crystallinity of more than 5% and         being at least partially cross-linked.         2. The polymer blend of paragraph 1 wherein the second polymer         is less crystalline than the thermoplastic first polymer.         3. The polymer blend of paragraph 1 or paragraph 2 wherein the         crystallinity difference between the second polymer and the         thermoplastic first polymer is less than 20%.         4. The polymer blend of any of paragraphs 1 to 3 wherein said         thermoplastic first polymer is a polymer of a C₂ to C₂₀ olefin.         5. The polymer blend of any of paragraphs 1 to 4 wherein said         thermoplastic first polymer is a polymer of propylene and from 0         to about 5% of an alpha-olefin by weight of the polymer.         6. The polymer blend of any of paragraphs 1 to 5 wherein the         thermoplastic first polymer has a melting point between about         100° C. and about 170° C.         7. The polymer blend of any of paragraphs 1 to 6 wherein the         thermoplastic first polymer has a melt flow rate of 2000 dg/min         or less, preferably 100 dg/min or less.         8. The polymer blend of any of paragraphs 1 to 7 wherein the         second polymer is produced from a plurality of comonomers         comprising at least one C₂ to C₂₀ olefin and at least one         polyene.         9. The polymer blend of paragraph 8 wherein said at least one         polyene has at least two polymerizable unsaturated groups.         10. The polymer blend any of paragraphs 1 to 9 wherein the         second polymer comprises propylene and from 2 to 15 weight % of         one or more C₂ and/or C₄ to C₁₀ alpha-olefin comonomers,         preferably ethylene.         11. The polymer blend of any of paragraphs 1 to 10 wherein at         least 4 wt % of the polymer blend is insoluble in xylene.         12. A process for producing the polymer blend of any of         paragraphs 1 to 11, the process comprising:

(i) polymerizing at least one first monomer to produce the thermoplastic first polymer; and

(ii) contacting at least part of said first polymer with at least one second monomer and at least one polyene under conditions sufficient to polymerize said second monomer to produce said second polymer and simultaneously cross-link said second polymer such that the product of said contacting (ii) comprises at least a fraction which is insoluble in xylene.

13. The process of paragraph 12 wherein said polymerizing (i) is conducted in the presence of a catalyst and said contacting (ii) is conducted in the presence of the same catalyst. 14. The process of paragraph 12 wherein said polymerizing (i) is conducted in the presence of a first catalyst and said contacting (ii) is conducted in the presence of a second catalyst different from the first catalyst. 15. The process of any one of paragraphs 12 to 14 wherein said polymerizing (i) is conducted in the presence of a single site catalyst comprising at least one catalyst component and at least one activator. 16. The process of any one of paragraphs 12 to 15 wherein the first polymer produced in (i) has at least 0.01% terminal unsaturation. 17. The process of any one of paragraphs 12 to 16 wherein (ii) comprises contacting at least part of said first polymer with a monomer mixture comprising at least 15 wt % of one or more C₃ to C₂₀ olefins and at least 0.0001 wt % of said at least one polyene. 18. The process of any one of paragraphs 12 to 17 and further including subjecting the product produced in (ii) to a curing step to increase the amount of said second polymer that is insoluble in xylene. 19. The process of paragraph 18 wherein, following said curing step, the amount of said second polymer insoluble in xylene comprises at least 10 wt % of said polymer blend.

The invention will now be more particularly described with reference to the Examples and the accompanying drawings.

In the Examples, molecular weights (number average molecular weight (Mn), weight average molecular weight (Mw), and z-average molecular weight (Mz)) were determined using a Waters 150 Size Exclusion Chromatograph (SEC) equipped with a differential refractive index detector (DR1), an online low angle light scattering (LALLS) detector and a viscometer (VIS). The details of these detectors as well as their calibrations have been described by, for example, T. Sun, P. Brant, R. R. Chance, and W. W. Graessley, in Macromolecules, Volume 34, Number 19, 6812-6820, (2001), incorporated herein by reference. Solvent for the SEC experiment was prepared by adding 6 grams of butylated hydroxy toluene (BHT) as an antioxidant to a 4 liter bottle of 1,2,4 trichlorobenzene (TCB) (Aldrich Reagent grade) and waiting for the BHT to solubilize. The TCB mixture was then filtered through a 0.7 micron glass pre-filter and subsequently through a 0.1 micron Teflon filter. There was an additional online 0.7 micron glass pre-filter/0.22 micron Teflon filter assembly between the high pressure pump and SEC columns. The TCB was then degassed with an online degasser (Phenomenex, Model DG-4000) before entering the SEC. Polymer solutions were prepared by placing dry polymer in a glass container, adding the desired amount of TCB, then heating the mixture at 160° C. with continuous agitation for about 2 hours. All quantities were measured gravimetrically. The TCB densities used to express the polymer concentration in mass/volume units were 1.463 g/ml at room temperature and 1.324 g/ml at 135° C. The injection concentration ranged from 1.0 to 2.0 mg/ml, with lower concentrations being used for higher molecular weight samples.

The branching index in the Examples was measured using SEC with an on-line viscometer (SEC-VIS) and is reported as g′ at each molecular weight in the SEC trace. The branching index g′ is defined as:

$g^{\prime} = \frac{\eta_{b}}{\eta_{l}}$

where η_(b) is the intrinsic viscosity of the branched polymer and η₁ is the intrinsic viscosity of a linear polymer of the same viscosity-averaged molecular weight (M_(v)) as the branched polymer. η₁=KM_(v) ^(α), K and α were measured values for linear polymers and should be obtained on the same SEC-DRI-LS-VIS instrument as the one used for branching index measurement. For polypropylene samples presented in this invention, K=0.0002288 and α=0.705 were used. The SEC-DRI-LS-VIS method obviates the need to correct for polydispersities, since the intrinsic viscosity and the molecular weight were measured at individual elution volumes, which arguably contain narrowly dispersed polymer. Linear polymers selected as standards for comparison should be of the same viscosity average molecular weight, monomer content and composition distribution. Linear character for polymer containing C2 to C10 monomers is confirmed by Carbon-13 NMR using the method of Randall (Rev. Macromol. Chem. Phys., C29 (2&3), p. 285-297). Linear character for C11 and above monomers is confirmed by GPC analysis using a MALLS detector. For example, for a copolymer of propylene, the NMR should not indicate branching greater than that of the co-monomer (i.e. if the comonomer is butene, branches of greater than two carbons should not be present). For a homopolymer of propylene, the GPC should not show branches of more than one carbon atom. When a linear standard is desired for a polymer where the comonomer is C9 or more, one can refer to T. Sun, P. Brant, R. R. Chance, and W. W. Graessley, Macromolecules, Volume 34, Number 19, 6812-6820, (2001) for protocols on determining standards for those polymers. In the case of syndiotactic polymers, the standard should have a comparable amount of syndiotacticty as measured by Carbon 13 NMR. The viscosity averaged g′ was calculated using the following equation:

$g_{vis}^{\prime} = \frac{\sum{C_{i}\left\lbrack \eta_{i} \right\rbrack}_{b}}{\sum{C_{i}{KM}_{i}^{\alpha}}}$

Where C_(i) is the polymer concentration in the slice i in the polymer peak, and [η_(i)]_(b) is the viscosity of the branched polymer in slice i of the polymer peak, and M_(i) is the weight averaged molecular weight in slice i of the polymer peak measured by light scattering, K and α are as defined above.

Peak melting point (Tm) and peak crystallization temperature (Tc) were determined by Differential Scanning calorimetry using the following procedure according to ASTM E 794-85. Crystallinity was calculated using heat of fusion determined using ASTM D 3417-99. Differential scanning calorimetric (DSC) data were obtained using a TA Instruments model Q100 machine. Samples weighing approximately 5-10 mg were sealed in aluminum sample pans. The DSC data were recorded by first cooling the sample to −100° C. and then gradually heating it to 200° C. at a rate of 10° C./minute. The sample was kept at 200° C. for 5 minutes before a second cooling-heating cycle was applied. Both the first and second cycle thermal events were recorded. Areas under the melting curves were measured and used to determine the heat of fusion and the degree of crystallinity. The percent crystallinity is calculated using the formula, [area under the curve (Joules/gram)/B (Joules/gram)]*100, where B is the heat of fusion for the homopolymer of the major monomer component. These values for B were obtained from the Polymer Handbook, Fourth Edition, published by John Wiley and Sons, New York 1999. A value of 189 J/g (B) was used as the heat of fusion for 100% crystalline polypropylene. A value of 290 J/g is used for the heat of fusion for 100% crystalline polyethylene. For polymers displaying multiple cooling and melting peaks, all the peak crystallization temperatures and peaks melting temperatures were reported. The heat of fusion for each melting peak was calculated individually.

The glass transition temperature (Tg) was measured by ASTM E 1356 using a TA Instruments model Q100 machine.

Morphology data were obtained using an Atomic Force Microscope (AFM) in tapping phase. All specimens were analyzed within 8 hours after cryofacing to prevent specimen relaxation. During cryofacing, the specimens were cooled to −130° C. and cut with diamond knives in a Reichert cryogenic microtome. They were then stored in a dissector under flowing dry nitrogen gas to warm up to ambient temperatures without condensation being formed. Finally, the faced specimens were mounted in a miniature steel vise for AFM analysis. The AFM measurements were performed in air on a NanoScope Dimension 3000 scanning probe microscope (Digital Instrument) using a rectangular 225-mm Si cantilever. The stiffness of the cantilever was ˜4 N/m with a resonance frequency of ˜70 kHz. The free vibration amplitude was high, in the range of 80 nm to 100 nm, with a RMS setting of 3.8 volts. While the set point ratio was maintained at a value equal to or lower than 0.5, the contact set point was adjusted routinely to ensure repulsive contacts with positive phase shifts. The cantilever was running at or slightly below its resonance frequency.

AFM phase images of all specimens were converted into a TIFF format and processed using PHOTOSHOP (Adobe Systems, Inc.). The image processing tool kit (Reindeer Games, Inc.) was applied for image measurements. Results of image measurements were written into a text file for subsequent data processing using EXCEL (Microsoft) or MATLAB (MathWorks, Inc.) for computing sizes/shapes of dispersed phases, co-continuity factor of co-continuous phases, or nearest-neighbor inter-particle distances.

Transmission Electron Microscopy (TEM) was used to study details of the interface between the ethylene/propylene/diene rubber and the semi-crystalline polypropylene phases. The instrument used was the JEOL 2000FX microscope. A heavy metal staining technique was employed to provide contrast to delineate the details of the sample morphology. Ruthenium tetroxide provides excellent contrast between amorphous and crystalline regions and was used. Lower density and amorphous polymers take up more stain than do higher density and more crystalline components. Thus heavily stained components appear darker in TEM amplitude contrast images whereas less heavily stained materials appear lighter. The TEM analytical method used involved:

-   -   Setting the orientation of the plane of analysis. Typically the         MD-ND (machine direction/normal direction) plane is preferred         for samples that may be oriented in the machine direction.     -   Creating a deformation-free face through the bulk polymer sample         using a cryomicrotome.     -   Staining with ruthenium tetroxide vapor for about 8 hours.     -   Cutting and collecting ultrathin (about 100 nm) sections from         the stained face using an ultramicrotome. The cutting is done         using a diamond knife. Sections are floated onto TEM grids.     -   Loading sections into the TEM for examination at the appropriate         accelerating voltage (typically 160 to 200 kV).     -   Examining the sections to determine level of sampling needed.     -   Acquiring digital images using appropriate vendor software.

The ethylene content of ethylene/propylene copolymers was determined using FTIR according to the following technique. A thin homogeneous film of polymer, pressed at a temperature of about 150° C., was mounted on a Perkin Elmer Spectrum 2000 infrared spectrophotometer. A full spectrum of the sample from 600 cm⁻¹ to 4000 cm⁻¹ was recorded and the area under propylene band at ˜1165 cm⁻¹ and the area of ethylene band at ˜732 cm⁻¹ in the spectrum were calculated. The baseline integration range for the methylene rocking band is nominally from 695 cm⁻¹ to the minimum between 745 and 775 cm⁻¹. For the polypropylene band the baseline and integration range is nominally from 1195 to 1126 cm⁻¹. The ethylene content in wt. % was calculated according the following equation:

ethylene content (wt. %)=72.698−86.495X+13.696X ²

where X=AR/(AR+1) and AR is the ratio of the area for the peak at ˜1165 cm⁻¹ to the area of the peak at ˜732 cm⁻¹.

Solvent extraction was used to isolate the different polymer species of the in-reactor polymer blends. The fractionations were carried out in a two-step successive solvent extraction when the polymer blend did not contain any oil: one involving cyclohexane extraction, the other xylene Soxhlet extraction. In the cyclohexane solvent extraction, about 0.3 gram of polymer was placed in about 60 ml of cyclohexane. The mixture was continuously stirred at room temperature for about 48 hours. The soluble fraction (referred as cyclohexane solubles) was separated from the insoluble material (referred as cyclohexane insolubles) using filtration under vacuum. The insoluble material was then subjected to the xylene soxhlet extraction procedure. In this step, the insoluble material from the room temperature cyclohexane extraction was first extracted for about 24 hours with xylene. The xylene insoluble portion (referred as xylene insolubles) was recovered by filtration and is the extract containing the at least partially cross-linked second polymer. The remaining portion was cooled down to room temperature and retained in a glass container for 24 hours for precipitation. The precipitated component (referred as xylene precipitate) was recovered through filtration and the soluble component (referred as xylene soluble) was recovered by evaporating the xylene solvent. In the case of blends containing paraffinic oil plasticizer and the like, another Soxhlet solvent extraction step was performed on the sample for 24 hours to isolate the oil from the blend before the cyclohexane extraction and xylene Soxhlet extraction using an azeotrope of acetone and cyclohexane in the ratio 2:1 by volume. The calculation of percent of xylene insolubles takes into account only the component directly from the polymerization reactors. Oil content or other post reactor additives was excluded.

In order to measure the physical properties of the polymer blends, samples were first mixed in a Brabender melt mixer with ˜45 mL mixing head. The polymer was stabilized with antioxidant during mixing in the Brabender. The Brabender was operated at 100 rpm and at temperature of 180° C. Mixing time at temperature was 5-10 minutes, after which the sample was removed from the mixing chamber. The homogenized samples were molded under compression into film on a Carver hydraulic press for analysis. About 7 grams of the homogenized polymer were molded between brass platens lined with Teflon™ coated aluminum foil. A 0.033 inch (0.08 cm) thick chase with a square opening 4 inch×4 inch (10.2×10.2 cm) was used to control sample thickness. After one minute of preheat at 170° C. or 180° C., under minimal pressure, the hydraulic load was gradually increased to 10,000 to 15,000 lbs, at which it was held for three minutes. Subsequently the sample and molding plates were cooled for three minutes under 10,000 to 15,000 lbs load between the water-cooled platens of the press. Plaques were allowed to equilibrate at room temperature for a minimum of 24 hours prior to physical property testing.

β relaxation, Loss Modulus (E″) and Storage Modulus (E′) were measured by dynamic mechanical thermal analysis (DMTA). The instrument used was the RSA II, Rheometrics Solid Analyzer II from TA Instruments, New Castle, Del. The instrument was operated in tension mode and used molded rectangular samples. Sample conditions were: 0.1% strain, 1 Hz frequency, and 2° C. per minute heating rate, covering the temperature range from −135° C. to the melting point of the sample. Samples were molded at about 200° C. Typical sample dimensions were 23 mm length×6.4 mm width×thickness between 0.25 mm and 0.7 mm, depending on the sample. Tan δ is the ratio of E″/E′. The output of these DMTA experiments is the storage modulus (E′) and loss modulus (E″). The storage modulus measures the elastic response or the ability of the material to store energy, and the loss modulus measures the viscous response or the ability of the material to dissipate energy. The ratio of E″/E′ (=tan δ) gives a measure of the damping ability of the material. Energy dissipation mechanisms (i.e., relaxation modes) show up as peaks in tan δ, and are associated with a drop in E′ as a function of temperature. The uncertainty associated with reported values of E′ is expected to be on the order of ±10%, due to variability introduced by the molding process.

Shore hardness was determined according to ISO 868 at 23° C. using a Durometer.

Stress-strain properties such as ultimate tensile strength, ultimate elongation, and 100% modulus were measured on 2 mm thick compression molded plaques at 23° C. by using an Instron testing machine according to ISO 37.

Compression set test was measured according to ISO 815A.

Tension set was measured according to ISO 2285.

Oil swell (oil gain) was determined after soaking a die-cut sample from compression molded plaque in IRM No. 3 fluid for 24 hours at 125° C. according to ASTM D 471.

Laboratory capillary viscosity (LCR) was measured using a Laboratory Capillary Rheometer according to ASTM D 3835-02 using a Dynisco Capillary rheometer at 30:1 L/D (length/diameter) ratio, a shear rate of 1200 l/s and a temperature of 204° C. The entrance angle of the laboratory capillary rheometer is 180°, barrel diameter is 9.55 mm. The heat soak time is 6 minutes.

Example 1

A polymer blend was produced in a two-stage polymerization reaction by polymerizing propylene in a first stage to make homopolymer, and copolymerizing propylene and ethylene as well as a diene cross-linking agent in a second stage in the presence of the homopolymer produced in the first stage. The polymerization was carried out in a 1-liter autoclave reactor equipped with a stirrer, an external water/steam jacket for temperature control, a regulated supply of dry nitrogen, ethylene, propylene, and a septum inlet for introduction of other solvents, catalysts and scavenger solutions. The reactor was first washed using hot toluene and then dried and degassed thoroughly prior to use. All the solvents and monomers were purified by passing through a 1-liter basic alumina column activated at 600° C., followed by a column of molecular sieves activated at 600° C. or Selexsorb CD column prior to transferring into the reactor.

In the first stage of polymerization, triisobutyl aluminum (TIBAL) (25 wt % in hexane, purchased from Sigma-Aldrich) solution was first added to the reactor. Then the catalyst solution was cannulated into the reactor using solvent. In succession, solvent (diluent) and propylene were added into the reactor. All of these were conducted at room temperature. The mixture was then stirred and heated to a desired temperature. The first stage of polymerization was ended when the desired amount of polypropylene was produced, determined by monitoring the reactor pressure during the reaction. Thereafter, the reactor was depressurized by venting the unreacted propylene and solvent to the atmosphere until the reactor pressure reached about 80 psig (544 kPa) to maintain an inert atmosphere in the reactor for the continuation of polymerization in the second stage.

In the second stage of polymerization, propylene was added into the mixture produced in the first stage. The mixture was then stirred and heated to a desired reaction temperature. In succession, ethylene and diene were added into the reactor. The ethylene was fed on demand to maintain a relative constant reactor pressure during the polymerization reaction. The ethylene consumption was monitored during the reaction using a mass flow meter. The polymerization reaction was terminated when desired amount of rubber was produced. Thereafter, the reactor was cooled down and unreacted monomer and solvent (diluent) were vented to the atmosphere. The resulting mixture, containing mostly solvent, polymer and unreacted monomers, was collected in a collection box and first air-dried in a hood to evaporate most of the solvent, and then dried in a vacuum oven at a temperature of about 90° C. for about 12 hours.

1,9-decadiene was used as the diene cross-linking agent in the second polymerization stage. The 1,9-decadiene was obtained from Sigma-Aldrich and was purified by first passing through an alumina column activated at high temperature under nitrogen, followed by a molecular sieve activated at high temperature under nitrogen.

Rac-dimethylsilyl bis(2-methyl, 4-phenylindenyl)zirconium dimethyl catalyst preactivated with N,N-dimethylanilinium tetrakis (pentafluorophenyl) borate (both obtained from Albemarle) at a molar ratio of about 1:1 in toluene was fed into the reactor in Stage 1. The same catalyst was used in the second stage of polymerization. Details of the experimental conditions, catalysts employed and the properties of the resultant polymer blend are listed in Table 1A below.

TABLE 1A Polymerization in Stage 1 Reaction temperature (° C.) 70 Amount of catalyst (mg) 0.84 Propylene #1 (ml) 150 Hexane (ml) 250 TIBAL (25 wt % in Toluene) (ml) 2 Reaction time1 (min) 6.2 Polymerization in Stage 2 Reaction temperature (° C.) 70 Propylene2 (ml) 200 Ethylene head pressure (psi) 80 1,9 decadiene (ml) 0.3 Reaction time2 (min) 20 Yield (g) 70.7 Tm (° C.) 157.6 Tc (° C.) 117.0 Heat of fusion (J/g) Tg (° C.) −18.7 Ethylene content (wt %) 6 Xylene precipitate (wt %) Xylene insolubles (wt %) Xylene solubles (wt %) Cyclohexane solubles (wt %)

The Tg value shown in Table 1A above refers to the elastomer component in the reactor-produced polymer blend. The value provides an indication of the amorphous nature of the elastomer component. The Tg of the polypropylene component—located primarily in the xylene precipitate fraction—is generally about 0° C., typical for semi-crystalline propylene homopolymers.

The morphology of the in-reactor blend produced in Example 1A was examined using AFM according to the procedure described above and the results are shown in FIG. 1A. A homogenous solid-state morphology was observed.

The strain-stress properties of the product of Example 1 are listed in Table 1B.

TABLE 1B Stress at 100% strain (psi) 2614.78 Stress at 500% strain (psi) 3626.81 Peak Stress (psi) 5132.36 Strain At Break (%) 946.24 Break Stress (psi) 5132.36 Initial modulus (psi) 21388.33 Energy To Break (in * lbf) 17.46 TOUGHNESS (in * lbf/in{circumflex over ( )}3) 106930.6

Example 2

The polymerization was carried out in a 2-liter autoclave reactor equipped similarly to the one used in Example 1. In the first stage of polymerization, 3 ml of tri-n-octylaluminum (TNOA) (25 wt. % in hexane, Sigma Aldrich) solution was first added to the reactor. In succession, solvent (diluent) and propylene were added into the reactor. All of these were conducted at room temperature. The mixture was then stirred and heated to the desired temperature for the first polymerization stage. Then the catalyst solution was cannulated into the reactor using additional propylene. The first stage of polymerization was ended when the desired amount of polypropylene was produced. Thereafter, the reactor was heated up to the desired temperature of the second polymerization stage. About 6-12 ml of air was injected into the reactor with about 100 ml of additional solvent to partially deactivate the catalyst used in the first stage of polymerization. The reaction medium was kept under proper mixing for about 8˜15 minutes to allow good catalyst-air contact prior to second stage of polymerization. The reactor was then pressurized to about 400 psig with ethylene. Then, in succession, diene, additional scavenger (TNOA or TEAL) and the second catalyst solution were added into the reactor. Additional ethylene was fed into the reactor, and the ethylene was fed on demand to maintain a relatively constant reactor pressure during the second polymerization reaction. The second polymerization reaction was terminated when desired amount of rubber was produced. Thereafter, the reactor was cooled down and unreacted monomer and solvent (diluent) were vented to the atmosphere. The resulting mixture, containing mostly solvent, polymer and unreacted monomers, was collected in a collection box and first air-dried in a hood to evaporate most of the solvent, and then dried in a vacuum oven at a temperature of about 90° C. for about 12 hours.

Rac-dimethylsilyl bis(2-methyl-4-phenylindenyl) zirconium dimethyl catalyst (Catalyst A) was used in the first stage to produce polypropylene and [di(p-triethylsilylphenyl)methylene](cyclopentadienyl) (3,8-di-t-butylfluorenyl)hafnium dimethyl catalyst (Catalyst B) (obtained from Albemarle) was used in the second stage to produce ethylene propylene diene rubber. Both catalysts were preactivated by dimethylanilinum tetrakis (heptafluoro-2-naphthyl) borate at a molar ratio of 1:1 in toluene. Details of the experimental conditions, catalysts employed and the properties of the resultant polymer blends are listed in Table 2A below.

TABLE 2A Polymerization in Stage 1 Reaction temperature (° C.) 75 Amount of catalyst (mg) 0.55 Propylene #1 (ml) 700 Toluene (ml) 700 TNOA (25 wt. %) (ml) 3 Reaction time1 (min) 11 Polymerization in Stage 2 Reaction temperature (° C.) 75 Amount of catalyst (mg) 0.85 Ethylene head pressure (psi) 30 1,9 decadiene (ml) 40 Toluene (ml) 300 TNOA (25 wt %) (ml) 5 Reaction time2 (min) 18 Yield (g) 59.0 Tm (° C.) 149.7 Tc (° C.) 98.3 Heat of fusion (J/g) 38.0 Tg (° C.) −14.0 Ethylene content (wt %) Xylene precipitate (wt %) 45.6 Xylene insolubles (wt %) 36.9 Xylene solubles (wt %) 15.8 Cyclohexane solubles (wt %) 1.7

A sample of the blend produced in Example 2 was compounded with about 30% of paraffinic oil (Paralux 6001R, obtained from Chevron Oil Corporation) at an elevated temperature in a Brabender mixer, and molded under compression into plaques, and tested for thermoplastic elastomer applications. The silicon hydride was a polysiloxane with silicon hydride functionality. The performance data of the cured and uncured blends are listed in Table 2B.

TABLE 2B Polymer (%) 100 70 Paralux oil 6001R (wt. %) 30 Hardness 33D 79A Ultimate tension strength (psi) 2535 1348 Ultimate elongation (%) 371 163 100% Modulus (psi) 1435 933 LCR viscosity 12001/s (Pa-s) 108 Tension set (%) 32 19 Compression set, 70° C./22 Hrs (%) 56 38 Weight gain, 121° C./24 hrs (%) 208 93 While the present invention has been described and illustrated by reference to particular embodiments, those of ordinary skill in the art will appreciate that the invention lends itself to variations not necessarily illustrated herein. For this reason, then, reference should be made solely to the appended claims for purposes of determining the true scope of the present invention. All documents described herein are incorporated by reference herein, including any priority documents and/or testing procedures to the extent they are not inconsistent with this text. Likewise, the term “comprising” is considered synonymous with the term “including” for purposes of Australian law. 

1. A homogeneous polymer blend having one glass transition temperature indicated on a dynamic mechanical thermal analyzer trace of tan δ versus temperature comprising: (a) a thermoplastic first polymer having a crystallinity of at least 30% and a melting temperature at or above 100° C., wherein said thermoplastic first polymer is a polymer of propylene and from 0 to about 5% of an alpha-olefin, by weight of the polymer; and (b) a second polymer different from the first polymer having a crystallinity less than that of the first polymer and being at least partially cross-linked, and (c) at least one polyene having at least two polymerizable unsaturated groups and said second polymer is a polymer of propylene, 2 to 15 weight % of one or more C₂ and/or C₄ to C₁₀ alpha-olefins comonomers and 0.01 to 5 wt % diene.
 2. (canceled)
 3. The polymer blend of claim 2 wherein the crystallinity difference between the second polymer and the thermoplastic first polymer is less than 20%.
 4. The polymer blend of claim 1 wherein said thermoplastic first polymer is a polymer of a C₂ to C₂₀ olefin.
 5. (canceled)
 6. The polymer blend of claim 1 wherein the thermoplastic first polymer has a melting point between about 100° C. and about 170° C.
 7. The polymer blend of claim 1 wherein the thermoplastic first polymer has a melt flow rate of 2000 dg/min or less.
 8. The polymer blend of claim 1 wherein the thermoplastic first polymer has a melt flow rate of 100 dg/min or less. 9-11. (canceled)
 12. The polymer blend of claim 1 wherein the comonomer is ethylene.
 13. The polymer blend of claim 1 wherein the second polymer comprises at least a fraction which is insoluble in xylene.
 14. The polymer blend of claim 13 wherein said fraction insoluble in xylene comprises at least is at least 4 wt % of the polymer blend.
 15. The polymer blend of claim 1 wherein said polymer blend is substantially free of processing oil and/or a curative agent. 16-35. (canceled) 